STRONG precision crepe tape
CRPTPE-PREC-STRONG-25MMX50M
Art.-no. 0992000525
EAN 4046777354294
Register now and access our wide range of products
Extra-thin, smooth, fibre-reinforced washi paper
- Due to the fibre reinforcement, the tape is particularly sturdy and tear-resistant, but remains flexible - ideal for multi-layer or film-forming material applications.
- For super-sharp paint edges without paint running.
- The supple material allows very precise bonding.
- Brilliantly suited for both solvent- and water-based paint systems.
High adhesive strength and can be removed without leaving residues
- Excellent adhesion with high adhesive strength due to the special adhesive.
- Suitable for most smooth, rough and uneven substrates.
- Due to the higher adhesive strength, it can also be used on slightly damp surfaces.
- The crepe tape has excellent strength when wet, making it suitable for wet sanding.
Heat- and UV-resistant
- The UV resistance of up to 6 months (in central European climatic conditions) means that it is also suitable for longer-term bonding outdoors.
- Heat-resistant up to +150 °C for max. 1 hour and therefore excellent for painting work requiring oven drying.
- Wait until the tape is dry before removing it.
- Exercise caution with paints containing zinc or zinc oxide, since residues may be left.
- On critical substrates such as parquet, laminate, cork, linoleum or other surfaces that will be visible later, adhesive residues or substrate tearing cannot be ruled out.
- When grouting tiles with sealant, the tape must be removed before the drying process is complete as otherwise the tape will be difficult to remove.
- Not suitable for use on carbon, zinc, lead (including lead-based paint), copper, anodised and zinc plated metals, artificial and natural stone (marble etc.) or aged or weathered PVC.
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
Datasheets(X)
- For masking work during painting and varnishing indoors and outdoors, on smooth to slightly rough substrates.
- Ideal for filling, varnishing and painting work and materials that can be diluted with water.
- Optimal for multi-layer or film-forming material application, e.g. brush rendering with subsequent coating.
- Also suitable for securing masking paper and masking films.
- For masking work when painting in the automotive, commercial vehicle, camper van, caravan and metalworking sectors.
- Ideal as masking tape for the automotive aftermarket.
- Also suitable for oven drying, multi-layer painting and tape-on-tape bonding.
- Can also be used on slightly damp substrates, such as surfaces with morning dew.
The surfaces on which the adhesive tape is applied must be dry and free of dust, oil, solvents or other chemicals.
Adhesive base | Acrylate |
Adhesive tape backing material | Fiber-reinforced japanese rice paper (washi tape) |
Colour | Orange |
Width | 25 mm |
Length | 50 m |
Thickness | 110 µm |
Min./max. processing temperature | 10 to 40 °C |
Min./max. temperature resistance | 0 to 100 °C |
Short term temperature resistance max. /conditions | 150 °C / short-term, one hour |
Dynamic peel strength at 25 mm | 5 N |
Elongation at break/conditions | 8 % / in accordance with DIN EN 14410 |
Resistance to tearing | 34 N/cm |
Ultraviolet resistance | 6 months, outdoor weathering |
Moisture resistance | Yes |
Shelf life from production/conditions | Unlimited / Cool, dry, frost-free, UV-protected storage at 18° to 21 °C and max. 65% relative humidity |